Nickel(II) pulveris oxydi (Ni Assay Min.78%) CAS 1313-99-1
Nickel(II) Oxide
| Synonym: | Nickel Monoxidum, Oxonickel |
| CAS NO: | 1313-99-1 |
| Formulae chemica | NiO |
| Molar massa | 74.6928g/mol |
| Aspectus | viridi crystallinum solidum |
| Density | 6.67g/cm3 |
| Liquescens punctum | 1,955°C(3,551°F; 2,228K) |
| Solubilitas in aqua | insensibilis |
| Solubilitas | dissolvere in KCN * |
| Susceptibilitas magnetica (χ) | +660.0·10−6cm3/mol |
| Index refractivus (nD) | 2.1818 |
Inceptum Specificationis pro Nickel(II) Oxide
| Symbolum | Nickel ≥(%) | Peregrinatio, Matth.≤ (%) | |||||||||||
| Co | Cu | Fe | Zn | S | Cd | Mn | Ca | Mg | Na | Insolubilis Hydrochloric acid(%) | Particula | ||
| UMNO780 | 78.0 | 0.03 | 0.02 | 0.02 | - | 0.005 | - | 0.005 | - | - | D50 Max.10μm | ||
| UMNO765 | 76.5 | 0.15 | 0.05 | 0.10 | 0.05 | 0.03 | 0.001 | - | 1.0 | 0.2 | 0.154mm pondus tentoriumresiduumMax.0.02% | ||
Sarcina: In situla stipata et intus conglutinatione ethene signata, pondus rete est 25 chiliogramma per situlam;
Quid est Nickel (II) Oxide adhibitum?
Nickel (II) Oxide adhiberi potest ad varias applicationes speciales et generaliter, applicationes distinguunt inter "gradum chemicum", quod est relative pura materia applicationum specialitatis et "gradus metallicus", quae maxime adhibentur ad mixtorum productionem.In ceramica industria adhibetur ad fricta, ferrites, ac fictilia vitreae.Oxydum sintered adhibitum ad mixturas chalybeas producendas.Solet est insolubilis in solutionibus aqueis (aquarum) et valde stabilis, utilia in structuris ceramicis efficiens tam simplex quam argillas ad electronicas provectas producens et leve pondus structurarum partium in aerospace et electronicis applicationibus sicut cibus cellulis in quibus ionica conductivity exhibent.Nickel Monoxide saepe reflectitur cum acida ad formandum sales (sulfel nickel), quae efficacia sunt ad electroplates et semiconductores producendos.NiO communis usus est foraminis onerariis materiae in tenuibus cellulis cinematographicis solaris.Nuper NiO adhibitum est ut gravidae NiCd rechargebiles in multis electronicis machinis inventae sint donec evolutionem in altilium environmentally- NiMH superiori.NiO materia electrochromica anodica, late pervestigata est ut electrodes occurro cum oxydatu, materia electronico-cathodica, in machinis electrochromicis complementariis.